高比重95钨镍铁石油加重杆产品详情：
1）比重大：一般比重为16.5-18.75g/cm3；
2）强度高：抗拉强度为700-1000Mpa；
3）吸收射线能力强：比铅高30-40%；
4）导热系数大：钨合金的导热系数为模具钢的5倍；
5）热膨胀系数小：只有铁或钢的1/2-1/3，
6）良好的可导电性能；无因为其良好的导电性能而广泛应照明和电焊行业
7）具有良好的可焊性和加工性。
8）株洲民成硬质合金可按您的要求生产各种形状、尺寸规格高比重合金。
高比重95钨镍铁石油加重杆具有高密度，高熔点，体积小，高耐磨性，硬度，高抗拉强度，高延伸性,耐高温等许多优良的特性。钨合金产品广泛应工业领域。
Tungsten alloy rod has so many advantages, such as high density, high melting point, small
volume, excellent hardness, superior wearing resistance, high ultimate tensile strength, high
ductility, high temperature resistance, etc. Tungsten alloys are widely used in many industrial
sectors.
什么是钨合金棒？
What is Tungsten Alloy Rod?
钨合金棒的制作流程是首先将钨粉末和其他金属粉末混合，压制，而后烧结成毛坯状半成品，毛坯状半成品经过旋锻和切削加工之后，*后制成钨合金棒。这些钨合金棒可根据客户需求制作成任意长度的，表面是光滑的，直径在3mm 以上。中空的管壁是3mm 以内。钨合金棒可以加工成中空状的。特殊的长度以及结构可根据客户的需求进行加工。
Tungsten alloy rod is produced by mixing and pressing tungsten and other metal powders and sintering them into semi-product billets, which is worked by rolling or swaging into rod. It can beproduced into any lengths as per requirement of customer with a smooth surface at diameters morethan 3mm, and diameter of hollow tube wall is below 3mm. Tungsten alloy rod can be machinedinto hollow type. Specific lengths and special fabrications can be supplied upon request.
高比重95钨镍铁加重杆用途
Applications for Tungsten Alloy Rod
由于钨合金棒具有高密度性，所以钨合金棒的主要用途是作为配重件控制和分配重量。钨合金棒可以进一步加工成配重件。
We have a large amount of tungsten alloy rod stock for sale. Most of the major applications
for tungsten alloy rod are based on its very high density where it is used to control or distributeweight in some way. The product can be machined further.
株洲民成硬质合金提供的钨合金棒可以配重件、辐射屏蔽件、产品、焊接棒、模具等等。一些体育用品也用到钨合金棒，比如飞镖，高尔夫球杆等。此外，由于钨合金的特性和Anviloy 1150 类似，所以钨合金也可以作为Anviloy 1150的替代品。
MC carbide can offer tungsten alloy rods and parts as counterweight,radiation shielding, military defense applications, welding rods, extrusion dies. Some sports also need alloy rods, such as darts, billets, golf club, etc. In addition, tungsten alloy can be acted as the replacement of Anviloy 1150, with very similar properties.